Details：

Beryllium nitride

Molecular weight: 55.05

Melting point:2200℃

Appearance: white powder

Characters: It is hard metal and refractory metal, soluble in water and will release nitrogen in acid solution and aqueous alkali. It can easy be oxygenated at 600℃ or above.

Use: Mainly used for refractory material

Aluminum nitride  

Molecular weight: 40.99

Molecular formular: AlN

Density: 2.18g/cm3

Use: used for crucible of smelting of Aluminum, Copper, Silver and Lead

Boron nitride

Melting point:2967℃

Density:2.18g/cm3

Main Application: Mainly used for alloy, high temperature resistant material, semiconductor and lubricating agent.

Silicon Nitride

Molecular formular: Si3N4

Relative quality: 1402.8

Appearance: off-white powder 

Density:3.44

Hardness: 9~9.5, the knoop hardness is approx 2200, the micro hardness is around 32630MPa

Melting point:1900℃(pressurized) 

Specific heat capacity: 0.71J/(g•K)

Heat of formation: -751.57kJ/mol

Thermal conductivity: 16.7W/(m•K)

Coefficient of linear expansion: 2.75×10-6/℃(20~1000℃)

Main Application: Mainly used in ceramic production, temperature resistant material, metallurgy and smelting and rubber industry

Titanium dioxide 

Molecular formular:TiO2

TiO2(W%)：≥90

Whiteness: ≥98%

Density:4.23

Melting point:2900℃

Boiling point:1855℃

Main Application: It is regarded as a best white paint and mainly used for coating, plastic, papermaking, printing ink, chemical industry and cosmetic industry

Titanium carbide    

Relative quality:59.91

Density:4.93g/cm3 

Melting point:3160℃

Boiling point:4820℃

Characters: It is high hardness, corrosion-resisting and good thermal stability

Main Application: mianly used for metal ceramic

Silicon carbide   

Specification: JIS#800, JIS#1000, JIS1200, JSS#1500, JIS#2000

Main Application: It is good for cutting equipment and kinds of diameter of cutting line.